اميد ايمان طلب

Ph.D. Dissertations

1. بررسي اثر آنيل بر رفتار الكتروشيميايي، مكانيكي و تريبولوژيكي پوشش‏هاي CrN/CrAlN اعمال‏شده به روش رسوب فيزيكي بخار
   يموراي ونگسا 2022
   Cathodic arc evaporated coatings contain residual stress due to the difference in the thermal coefficient between the substrate and the coating. Furthermore, the coating also contains defects such as pinholes and macroparticles which can be detrimental to the mechanical, tribological, and electrochemical properties of the deposited coatings. Post-deposition annealing has been proven to improve the properties of the material due to its ability to reduce residual stress and defects. The study aims to find the optimal annealing temperature for CrN/CrAlN coating and also evaluate the effect of annealing on the phases, hardness, wear, and corrosion. In this study, CrN/CrAlN multilayer coating was deposition AISI 304 substrates using the cathodic arc evaporation physical vapor deposition method (CAE-PVD). Thereafter, the samples were annealed in a vacuum furnace at 400, 500, 600, and 700 ℃. Characterization techniques were used to evaluate the effect of annealing on the mechanical properties, tribological behavior, and electrochemical properties of CrN/CrAlN multilayer coating. X-ray diffraction (XRD) was used to identify the phases, texture coefficient, and crystallite sizes. A scanning electron microscope (SEM) was used to analyze the surface morphology and also used to analyze the cross-section morphology. Energy Dispersive X-Ray Analysis (EDS) was utilized to analyze the elementary composition of the coating. An atomic force microscope (AFM) was used to analyze the surface topography and the roughness of the coating. The contact angle technique was used to evaluate the wettability of the coating. Rockwell-C adhesion test was used to evaluate the quality of the adhesion between the coating and the substrate. Nanoindentation test was used to investigate the evolution of the mechanical properties of the coating. The wear rate and wear morphology were characterized using a ball-on disk tribometer in ambient air and Ringer’s solution. The electrochemical properties of the
   Thesis summary
   
   
2. بررسي ارتباط معماري پوشش هاي نانوساختار نيتريد كروم و نيتريد زيركونيوم اعمال شده بر زيرلايه فولاد زنگ نزن AISI 304 به روش رسوب فيزيكي بخار (PVD) با رفتار الكتروشيميايي و مكانيكي آن ها
   پرويز محمديان صميم 2021
   هدف از انجام تحقيق حاضر، بررسي ارتباط معماري (تغيير تعداد لايه ها) پوشش هاي نانوساختار نيتريد كروم و نيتريد زيركونيوم اعمال شده بر زيرلايه فولاد زنگ نزن AISI 304 به روش رسوب فيزيكي از فاز بخار به كمك قوس كاتدي (CAE-PVD) با رفتار الكتروشيميايي و مكانيكي آن ها است. در اين تحقيق، پوشش هاي نانوساختار ZrN/CrN با جفت لايه هاي 10، 20 ،30 و هم چنين تك لايه CrN ايجاد شدند. پس از لايه نشاني، بررسي هاي ريزساختاري با استفاده از تصاوير ميكروسكوپ هاي الكتروني روبشي (SEM)و ميكروسكوپ الكتروني روبشي گسيل ميدان (FE-SEM) صورت گرفت و به منظور شناسايي فازهاي موجود در پوشش ها از الگوهاي پراش پرتو ايكس(XRD) استفاده شد. براي ارزيابي چسبندگي پوشش ها از روش سختي سنجي راكول C استفاده شد. زبري، سختي و تنش پسماند پوشش ها با استفاده از ميكروسكوپ نيروي اتمي (AFM) مجهز به نانوفرورونده ارزيابي شدند. رفتار الكتروشيميايي پوشش ها با استفاده از آزمون هاي پلاريزاسيون پتانسيوديناميك و طيف سنجي امپدانس الكتروشيميايي(EIS) در محيط هاي 5/3 درصد وزني كلريدسديم و رينگر بررسي شد.
   Thesis summary